DIY stainless steel conical beer fermenter Pt.1

Please search my blog for "fermenter" to find all of the posts regarding this project.

I am building a stainless steel tank that will eventually become a very unique beer-brewing vessel. My idea is to make a tank such that the entire process can take place without ever having to transfer the beer from one tank to another. This vessel will boil the wort, chill the wort, provide a temperature-controlled fermentation period, allow the trub to be removed, and provide a secondary fermentation. This tank was designed with my experience in brewing about 30 5-gallon batches of beer using the extract process. I don't have much inspiration to do all-grain brewing yet.

Having said all of that, I am also learning to TIG weld, and this project will provide many different welding setups -- all in stainless steel.


I bought a stainless steel conical hopper, model TMS14514 from
http://www.toledometalspinning.com/products/hoppers/priceList.asp

Toledo Metal Spinning sent the item very quickly, and I am impressed with the quality. The edges are extremely flat, and the overall finish and dimensional tolerances are great.

It holds 6.4 gallons total, so a 5 gallon batch of beer should fit pretty well. The hopper is a continuous piece with no hole in the bottom. I will be mounting a butterfly valve at the apex, so I need to cut the tip off to match the diameter of the valve housing. I knew before I ordered the hopper that I would only need to slice off about 1/8" off the end.

I used a slitting saw in my milling machine to do the job. This left me with a super flat clean edge. 70 RPM, 0.5 inches per minute, however the feed rate is measured at center of the saw, and I programmed a G2 circular path. This means the feed at the cutting point is probably lower. I had problems with chatter, thus necessitating this low feed rate.

This is one half of the butterfly valve housing after I welded it to the cone. The blue hose is silicone, and is carrying argon to the backside of the weld. In addition to the foil on top, I have made a dam with aluminum foil and tape inside the neck of the cone to trap the argon in the space around the weld.

Since the first weld went so well, I decided to weld on the inside of the fitting as well. Ultimately, this was not a great idea, but the weld itself went well. I used a copper tube with a line of tiny holes drilled in it to disperse backing argon to the outside of the cone. I had a fair bit of room inside the valve fitting for the TIG torch and filler rod.

I used a die grinder to smooth out the interior weld. After putting it together, it leaked! I had used the die grinder too much, and made the metal thin enough where a tiny pinhole in the weld made it all the way through the metal. I re-welded the outside bead, and then realized that I should have just made a couple of passes on the exterior to build up material. Then I could die-grind away the inside until I ground into the weld bead. No need to weld the interior. This would provide a nice smooth surface inside the tank and ensure there was enough material to keep it structurally sound.


It looks good now.


I originally started to cut this hole with a high-quality hole-saw in a corded drill. After a few seconds, I realized it was probably not going to work. Stainless is just such a tough metal, cutting tools just bounce off it. I used a free-hand plasma cutter to make the hole.

I made another aluminum foil/tape dam around the wall on the interior.


The weld went pretty well.



This time, I learned how to do it. Instead of welding on the inside, I just built up a nice bead, then used the die-grinder on the interior until I ground into the bead. It's nice and smooth on the inside.

Rust in the aquarium / Passivating stainless steel

OK, so I owe the titanium fanboys an apology. In my original post about aquarium chillers, I asserted that a stainless steel chiller coil would not rust in a saltwater aquarium. The coil in my tank rusted after about 6 months. Take a look:

I decided to sandblast the part so that I could see how extensive the damage was.

Yeow! The metal must have been exceptionally thin, and the sandblasting blew right through it!

I used 316 SS filler rod, and TIG welded the hole shut. The blue tube is an argon hose to protect the inside of the stainless tube from oxidation while welding.


Now it's all patched up. The heavy corrosion was localized around the area where the stainless coil entered the plastic filter box (see top picture) . My guess is that vibration from the pump caused the rough surface of the plastic to abrade the passivated layer on the stainless, thus causing a localized spot where the metal was unprotected. I've heard that passivated the stainless in an acid bath can create a stronger, more uniform passive layer. There are two common acids used to passivate stainless: nitric and citric. Nitric acid is nasty stuff, and it's possible to damage the stainless parts if the procedure is done incorrectly. Citric acid seems to be just as effective as nitric, and it's non-toxic. Here is the best reference on citric acid passivation:

http://www.astropak.com/downloads/technical_papers/boeing_passivation.pdf

I mixed a %15-by-weight solution of citric acid in water. I got 2lbs of citric acid on eBay for under $10 shipped. I submerged the stainless coil in the solution for 2 hours at room temperature. I could see the surface changed a bit -- the shade of gray was a little different. Hopefully this means it built up a nice strong oxide layer.

I've put the coil back into the aquarium, and added some silicone pads to the filter box so that the plastic would not scrape away at the stainless coil. I'll keep you updated to see how effective it is.

Bent TIG electrode = trailing shield?

Do you think this looks messed up?

Check out the welds that I can make with the messed up electrode. This is 1/16" 304:
I purposefully bent the electrode in the direction that I was moving the TIG torch. That way, there was a lot more gas coverage behind the arc than in front. It worked wonderfully! Even near the edge, the heat buildup was much less of a problem. I think the next step will be to make a trailing shield for the torch. Trailing shields are available, but only for amazingly high amounts of money. One alternative might be the "Monster nozzle". It could be large enough to act as a trailing shield.